Behr, Michael and Proff, Peter and Kolbeck, Carola and Langrieger, Sabine and Kunze, Johannes and Handel, Gerhard and Rosentritt, Martin (2011) The bond strength of the resin-to-zirconia interface using different bonding concepts. JOURNAL OF THE MECHANICAL BEHAVIOR OF BIOMEDICAL MATERIALS, 4 (1). pp. 2-8. ISSN 1751-6161,
Full text not available from this repository. (Request a copy)Abstract
Objectives. This study investigated the shear bond strength (SBS) and the tensile bond strength (TBS) of the zirconia-to-resin interface using different cement bonding concepts. Methods. Coplanar zirconia specimens were bonded to CoCr-cylinders measuring 5 mm in diameter and 3 mm in height. All bonding areas were first sandblasted with 110 lull Al(2)O(3) (0.28 MPa, 10 s). SBS and TBS were determined after 24 h and 90 d of water storage as well as after 12,000 thermal cycles (TC, 5 degrees/55 degrees C, 17 d). The bonding concepts consisted of the application of a silane coupling agent, tribological silica coating (Rocatec system), cements or primers containing phosphone, mono-phosphate, or di-phosphate, and a combination of silica coating and primer. Results. Bond strength higher than 10 MPa was considered clinically sufficient. SBS measured with each bonding concept surpassed this value, except control and MaxCem after 90 d. In contrast, TBS values were rather different. The application of a silane coupling agent alone showed very low values in the TBS test. Silica coating was only sufficient after 90 d of water storage and when combined with phosphate-esters or phosphone-containing primers. Bonding agents based on di-phosphates or phosphones showed stable TBS values of less than 10 MPa under different aging conditions. The predominant mode of failure was adhesive failure at the ceramic surface. Conclusions. None of the investigated bonding concepts of the zirconia-to-resin interface provided clinically sufficient tensile bond strength. SBS values were inadequate for a sufficient ranking. (C) 2010 Elsevier Ltd. All rights reserved.
| Item Type: | Article |
|---|---|
| Uncontrolled Keywords: | OXIDE CERAMIC CROWNS; LUTING AGENTS; SHEAR; RETENTION; TENSILE; CEMENTS; Shear bond strength; Tensile bond strength; Zirconia; Water storage; Silane coupling agent; Silica coating; Phosphate-ester |
| Subjects: | 600 Technology > 610 Medical sciences Medicine |
| Divisions: | Medicine > Lehrstuhl für Zahnärztliche Prothetik |
| Depositing User: | Dr. Gernot Deinzer |
| Date Deposited: | 01 Jul 2020 05:47 |
| Last Modified: | 01 Jul 2020 05:47 |
| URI: | https://pred.uni-regensburg.de/id/eprint/21619 |
Actions (login required)
 |
View Item |